Ultem PEI HU1010,物性
| 物理性能 | 額定值 | 單位制 | 測試方法 | ||
| 比重 | 1.27 | g/cm3 | ASTM D792, ISO 1183 | ||
| 熔流率（熔體流動速率） (337°C/6.6 kg) | 18 | g/10 min | ASTM D1238 | ||
| 溶化體積流率（MVR） (220°C/5.0 kg) | 25.0 | cm3/10min | ISO 1133 | ||
| 收縮率 - 流動 (3.20 mm) | 0.50 到 0.70 | % | 內部方法 | ||
| 吸水率 | ISO 62 | ||||
| 飽和, 23°C | 1.3 | % | |||
| 平衡, 23°C, 50% RH | 0.70 | % | |||
| 機械性能 | 額定值 | 單位制 | 測試方法 | ||
| 拉伸模量 | |||||
| -- 2 | 3580 | MPa | ASTM D638 | ||
| -- | 3200 | MPa | ISO 527-2/1 | ||
| 抗張強度 | |||||
| 屈服 3 | 110 | MPa | ASTM D638 | ||
| 屈服 | 105 | MPa | ISO 527-2/5 | ||
| 斷裂 3 | 105 | MPa | ASTM D638 | ||
| 斷裂 | 85.0 | MPa | ISO 527-2/5 | ||
| 伸長率 | |||||
| 屈服 3 | 7.0 | % | ASTM D638 | ||
| 屈服 | 6.0 | % | ISO 527-2/5 | ||
| 斷裂 3 | 60 | % | ASTM D638 | ||
| 斷裂 | 60 | % | ISO 527-2/5 | ||
| 彎曲模量 | |||||
| 50.0 mm 跨距 4 | 3420 | MPa | ASTM D790 | ||
| 100 mm 跨距 5 | 3520 | MPa | ASTM D790 | ||
| -- 6 | 3300 | MPa | ISO 178 | ||
| 彎曲應力 | |||||
| -- 6, 7 | 160 | MPa | ISO 178 | ||
| 屈服, 50.0 mm 跨距 4 | 174 | MPa | ASTM D790 | ||
| 屈服, 100 mm 跨距 5 | 165 | MPa | ASTM D790 | ||
| 泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 轉輪) | 10.0 | mg | ASTM D1044 | ||
| 沖擊性能 | 額定值 | 單位制 | 測試方法 | ||
| 簡支梁缺口沖擊強度 8 (23°C) | 3.0 | kJ/m2 | ISO 179/1eA | ||
| 懸壁梁缺口沖擊強度 | |||||
| -30°C | 35 | J/m | ASTM D256 | ||
| 23°C | 32 | J/m | ASTM D256 | ||
| -30°C 9 | 5.0 | kJ/m2 | ISO 180/1A | ||
| 23°C 9 | 5.0 | kJ/m2 | ISO 180/1A | ||
| 無缺口懸臂梁沖擊 (23°C) | 1300 | J/m | ASTM D4812 | ||
| 裝有測量儀表的落鏢沖擊 (23°C, Total Energy) | 33.0 | J | ASTM D3763 | ||
| 落錘沖擊 (23°C) | 33.9 | J | ASTM D3029 | ||
| 熱性能 | 額定值 | 單位制 | 測試方法 | |
| 載荷下熱變形溫度 | ||||
| 1.8 MPa, 未退火, 6.40 mm | 199 | °C | ASTM D648 | |
| 1.8 MPa, 未退火, 64.0 mm 跨距 10 | 193 | °C | ISO 75-2/Af | |
| 維卡軟化溫度 | ||||
| -- | 219 | °C | ASTM D1525 11 | |
| -- | 211 | °C | ISO 306/B50 | |
| -- | 212 | °C | ISO 306/B120 | |
| 線形熱膨脹系數 | ||||
| 流動 : -20 到 150°C | 5.6E-5 | cm/cm/°C | ASTM E831 | |
| 流動 : -40 到 40°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 | |
| 橫向 : -40 到 40°C | 5.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 | |
| 電氣性能 | 額定值 | 單位制 | 測試方法 | |
| 體積電阻率 | 1.0E+17 | ohm·cm | ASTM D257 | |
| 介電強度 | ASTM D149 | |||
| 1.60 mm, in Air | 33 | kV/mm | ||
| 1.60 mm, in Oil | 28 | kV/mm | ||
| 介電常數 (1 kHz) | 3.15 | ASTM D150 | ||
| 耗散因數 | ASTM D150 | |||
| 1 kHz | 1.3E-3 | |||
| 2.45 GHz | 2.5E-3 | |||
| 耐電弧性 12 | PLC 5 | ASTM D495 | ||
| 相比耐漏電起痕指數(CTI) | PLC 4 | UL 746 | ||
| 高電弧燃燒指數(HAI) | PLC 3 | UL 746 | ||
| 高電壓電弧起痕速率 (HVTR) | PLC 2 | UL 746 | ||
| 熱絲引燃 (HWI) | PLC 1 | UL 746 | ||
| 可燃性 | 額定值 | 單位制 | 測試方法 | |
| UL 阻燃等級 | UL 94 | |||
| 0.711 mm |
· V-2 · V-0 |
|||
| 3.00 mm | 5VA | |||
| 極限氧指數 | 44 | % | ASTM D2863 | |
| 注射 | 額定值 | 單位制 |
| 干燥溫度 | 149 | °C |
| 干燥時間 | 4.0 到 6.0 | hr |
| 干燥時間，最大 | 24 | hr |
| 建議的最大水分含量 | 0.020 | % |
| 建議注射量 | 40 到 60 | % |
| 料筒后部溫度 | 332 到 399 | °C |
| 料筒中部溫度 | 338 到 399 | °C |
| 料筒前部溫度 | 343 到 399 | °C |
| 射嘴溫度 | 343 到 399 | °C |
| 加工（熔體）溫度 | 349 到 399 | °C |
| 模具溫度 | 135 到 163 | °C |
| 背壓 | 0.345 到 0.689 | MPa |
| 螺桿轉速 | 40 到 70 | rpm |
| 排氣孔深度 | 0.025 到 0.076 | mm |