| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 物理性能 | 密度 | ASTM D792 |
1.19
|
g/cm³
|
|
| ISO 1183 | 1.20 |
g/cm³
|
|||
| 熔流率 | (300°C/1.2 kg) | ASTM D1238 |
5.0
|
g/10 min
|
|
| 溶化體積流率 | (300°C/1.2 kg) | ISO 1133 |
5.00
|
cm³/10min
|
|
|
收縮率
|
流動 (3.20 mm) | Internal Method |
0.55 到 0.75
|
% | |
|
橫向流動 : 3.20 mm
|
Internal Method |
0.60 到 0.80
|
% | ||
|
吸水率
|
飽和, 23°C
|
ISO 62 |
0.14
|
%
|
|
|
平衡, 23°C, 50% RH
|
ISO 62 |
0.11
|
%
|
||
|
室外適用性
|
f1
|
||||
| 機械性能 |
拉伸模量
|
5.0 mm/min | ASTM D638 |
2500
|
MPa |
| ISO 527-2/1 |
2400
|
MPa |
|||
|
抗張強度
|
屈服類型 1, 50 mm/min
|
ASTM D638 |
68
|
MPa
|
|
| 屈服 | ISO 527-2/50 | 67 |
MPa
|
||
|
斷裂類型 1, 50 mm/min
|
ASTM D638 |
52
|
MPa
|
||
| 斷裂 | ISO 527-2/50 | 52 |
MPa
|
||
|
伸長率
|
屈服類型 1, 50 mm/min
|
ASTM D638 |
6.0
|
%
|
|
| 屈服 | ISO 527-2/50 | 6.0 |
%
|
||
|
斷裂類型 1, 50 mm/min
|
ASTM D638 |
51
|
% | ||
| 斷裂 | ISO 527-2/50 | 23 |
%
|
||
|
彎曲模量
|
1.3 mm/min (50.0 mm 跨距) | ASTM D790 |
2400
|
MPa
|
|
| 2.0 mm/min | ISO 178 |
2500
|
MPa
|
||
|
彎曲強度
|
1.3 mm/min (屈服, 50.0 mm 跨距) | ASTM D790 |
106
|
MPa
|
|
| 2.0 mm/min | ISO 178 | 103 |
MPa
|
||
| 沖擊性能 |
簡支梁缺口沖擊強度80*10*3 sp=62mm
|
-30°C
|
ISO 179/1eA | 9.0 |
kJ/m²
|
|
23°C
|
ISO 179/1eA |
10
|
kJ/m²
|
||
|
簡支梁缺口沖擊強度
|
-30°C
|
ISO 179/1eU |
無斷裂
|
|
|
|
23°C
|
ISO 179/1eU |
無斷裂
|
|||
|
懸壁梁缺口沖擊強度
|
-30°C
|
ASTM D256 |
85
|
J/m
|
|
|
23°C
|
ASTM D256 | 100 |
J/m
|
||
|
-30°C 80*10*3
|
ISO 180/1A | 9.0 |
kJ/m²
|
||
|
23°C 80*10*3
|
ISO 180/1A | 10 |
kJ/m²
|
||
| 無缺口伊佐德沖擊強度 |
-30°C
|
ISO 180/1U |
無斷裂
|
||
| 23°C | ISO 180/1U |
無斷裂
|
|||
| 裝有測量儀表的落鏢沖擊 | (23°C, Total Energy) | ASTM D3763 |
66.0
|
J | |
| 熱性能 |
熱變形溫度
|
0.45 MPa, 未退火, 3.20 mm
|
ASTM D648 |
131
|
°C
|
|
0.45 MPa, 未退火, 100 mm 跨距120*10*4 mm
|
ISO 75-2/Be |
131
|
°C
|
||
|
1.8 MPa, 未退火, 3.20 mm
|
ASTM D648 |
120
|
°C
|
||
| 1.8 MPa, 未退火, 100 mm 跨距120*10*4 mm | ISO 75-2/Ae | 120 |
°C
|
||
|
維卡軟化溫度
|
標準 B (120°C/h), 壓 力2 (50N) | ASTM D1525 |
136
|
°C
|
|
| ISO 306/B50 | 137 |
°C
|
|||
| ISO 306/B120 | 139 |
°C
|
|||
|
Ball Pressure Test (125°C)
|
IEC 60695-10-2 | Pass | |||
|
線形膨脹系數
|
流動 (-40 到 40°C)
|
ASTM E831 |
0.000066
|
cm/cm/°C
|
|
|
流動 23 到 80°C)
|
ISO 11359-2 |
0.000072
|
cm/cm/°C
|
||
|
橫向 (-40 到 40°C)
|
ASTM E831 |
0.000070
|
cm/cm/°C
|
||
|
橫向 23 到 80°C
|
ISO 11359-2 |
0.000076
|
cm/cm/°C
|
||
|
RTI Elec
|
UL 746 |
125
|
°C
|
||
|
RTI Imp
|
UL 746 | 120 |
°C
|
||
|
RTI Str
|
UL 746 |
125
|
°C
|
||
| 電氣性能 |
介電常數
|
(1.10 GHz) | ASTM ES7-83 |
2.79
|
|
| 耗散因數 | (1.10 GHz) | ASTM ES7-83 |
0.0058
|
||
| 可燃性 |
UL 阻燃等級
|
0.400 mm
|
UL 94 |
V-2
|
|
|
1.00 mm
|
UL 94 |
V-0
|
|||
|
3.00 mm
|
UL 94 | 5VA | |||
|
灼熱絲易燃指數 (1.20mm)
|
IEC 60695-2-12 |
960
|
°C
|
||
|
熱燈絲點火溫度 (1.20 mm)
|
IEC 60695-2-13 | 875 |
°C
|
||
| 注射 |
干燥溫度
|
121 |
°C
|
||
|
干燥時間
|
3到4 |
hr
|
|||
| 干燥時間,最大 | 48 |
hr
|
|||
|
建議的最大水分含量
|
0.020 | % | |||
|
建議注入量
|
40 到 60
|
%
|
|||
|
螺筒后部溫度
|
266 到 288
|
°C
|
|||
|
螺筒中部溫度
|
277 到 299
|
°C
|
|||
|
螺筒前部溫度
|
288 到 310
|
°C
|
|||
|
射嘴溫度
|
282 到 304
|
°C
|
|||
|
加工（熔體）溫度
|
288 到 310
|
°C
|
|||
|
模具溫度
|
71.1 到 93.3
|
°C
|
|||
|
背壓
|
0.345 到 0.689
|
MPa
|
|||
|
螺桿轉速
|
40 到 70
|
rpm | |||
|
排氣孔深度
|
0.025 到 0.076
|
mm | |||